Q/L YS136-1988 Ntoatoaso a alumina –graphite a ɛyɛ hyew nneɛma a wɔde yɛ Con-casting
Nkyerɛmu
Saa Submerged Entry Nozzles yi yɛ cast refractory sleeves, a wɔde si tundish no ase na wɔde hyɛ mould level a ɛwɔ continuous steel casting equipment no ase. Wɔn botae ne sɛ wɔbɛbɔ dade no ho ban na ansen mfi tundish no mu akɔ crystallizer no mu, na wɔasiw oxidation a ɛto so abien ne dade a wɔabɔ no apetepete wɔ tundish no mu no ano. Bere koro no ara mu no, wodi dwuma titiriw wɔ slab no su a ɛbɛma atu mpɔn, adwumayɛ tebea a ɛkɔ anim, a ɛma casting adwuma a ɛkɔ so yɛ den ne slab no ani sintɔ a wosiw ano.
Su
Yɛn Submerged Entry Nozzles no yɛ dadeɛ a ɛkorɔn-quality, a ɛwɔ slag resistance pa, plugging resistance, service nkwa nna tenten, acidity a ɛba fam, na ɛtumi kura n’ahoɔden ne ne hwɛbea mu kyɛ. Wɔwɔ ahotew su, wobetumi asiw oxidation a ɛwɔ dade a wɔabɔ mu no ano na wɔ ɔkwan a etu mpɔn so siw dade a wɔabɔ no nsɛe ano. Bio nso, yɛhyɛ nyansa sɛ paw nsuo a wɔde hyɛ nsuo mu no nsusuiɛ a ɛfata sɛdeɛ ɔfa a wɔhwie gu no kɛseɛ ne ahoɔhare a wɔde hwie gu no teɛ, na ɛbɛtumi nso ama wo nnwuma a wɔayɛ ama wo.
Nnuru ne abɔde mu nneɛma a ɛwɔ nneɛma mu
Nipadua | Al2O3anti-nneɛma a wɔde siw ano | Slag line a wɔde kyerɛw nsɛm | Kyɛnsee | |||||
Adwumayɛ Tebea Ahorow | Preheating a wɔde yɛ ade | Ɛnyɛ-preheating | Argon a ɛyɛ hu | Ɛnyɛ-Argon | Ɛnyɛ-carbon | Z45 | ZSP na ɔkyerɛwee | Nneɛma a wɔde yɛ adwuma no yɛ Saa ara na The cooper -ative stopper |
Nnuru a wɔde yɛ nhwehwɛmu | ||||||||
Al2O3 % | Ɛboro anaasɛ ɛne 40.0 yɛ pɛ | Ɛboro anaasɛ ɛne no yɛ pɛ 45.0 | Ɛboro anaasɛ ɛne 43.0 yɛ pɛ | Ɛboro anaasɛ ɛne 65.0 yɛ pɛ | Ɛboro anaasɛ ɛne no yɛ pɛ 55.0 | |||
ZrO2 % | Ɛboro anaasɛ ɛne 35.0 yɛ pɛ | Ɛboro anaasɛ ɛne 75.0 yɛ pɛ | Ɛboro anaasɛ ɛne 65.0 yɛ pɛ | |||||
MgO % . | Ɛboro anaasɛ ɛne 18.0 yɛ pɛ | |||||||
C+SiC % 100. | Ɛboro anaasɛ ɛne 25.0 yɛ pɛ | Ɛboro anaasɛ ɛne 20.0 yɛ pɛ | Ɛboro anaasɛ ɛne 20.0 yɛ pɛ | Ɛboro anaasɛ ɛne 15.0 yɛ pɛ | Ennu anaasɛ ɛne 8.0 yɛ pɛ | Ɛboro anaasɛ ɛne 11.0 yɛ pɛ | Ɛboro anaasɛ ɛne 15.0 yɛ pɛ | |
Nneɛma a ɛwɔ nipadua mu | ||||||||
Nsuo a ɛyɛ den g/cm3 | Ɛboro anaasɛ ɛne 2.25 yɛ pɛ | Ɛboro anaasɛ ɛne 2.36 yɛ pɛ | Ɛboro anaasɛ ɛne 2.10 yɛ pɛ | Ɛboro anaasɛ ɛne 2.58 yɛ pɛ | Ɛboro anaasɛ ɛne 2.65 yɛ pɛ | Ɛboro anaasɛ ɛne no yɛ pɛ 3.50 | Ɛboro anaasɛ ɛne 3.30 yɛ pɛ | |
Ɛda adi sɛ Porosity % . | Ennu anaasɛ ɛne 19.0 yɛ pɛ | Ennu anaasɛ ɛne 19.0 yɛ pɛ | Ennu anaasɛ ɛne 25.0 yɛ pɛ | Ennu anaasɛ ɛne 21.0 yɛ pɛ | Ennu anaasɛ ɛne 20.0 yɛ pɛ | Ennu anaasɛ ɛne 22.5 yɛ pɛ | Ennu anaasɛ ɛne 20.0 yɛ pɛ | |
Awɔw mu Crushing Ahoɔden MPa | Ɛboro anaasɛ ɛne 19.0 yɛ pɛ | Ɛboro anaasɛ ɛne 20.0 yɛ pɛ | Ɛboro anaasɛ ɛne 10.0 yɛ pɛ | Ɛboro anaasɛ ɛne 18.0 yɛ pɛ | Ɛboro anaasɛ ɛne 18.0 yɛ pɛ | Ɛboro anaasɛ ɛne 16.0 yɛ pɛ | Ɛboro anaasɛ ɛne 16.0 yɛ pɛ | |
Moludus a Ɛma Paapae MPa | Ɛboro anaasɛ ɛne 6.0 yɛ pɛ | Ɛboro anaasɛ ɛne 6.0 yɛ pɛ | Ɛboro anaasɛ ɛne 6.0 yɛ pɛ | Ɛboro anaasɛ ɛne 3.0 yɛ pɛ | ||||
Tags a ɛyɛ hyew .: nsu ase hyɛn nozzles, China nsu ase entry nozzles suppliers, adwumayɛbea